High Strength 60/80/100/130/200kg/M3 PVC Core Foam Yacht Construction Boat PVC Foam

Basic Info

Model NO.	RG-PVC00001
Tensile Strength	81~130MPa
MOQ	10sqm
Sample	Free Sample
Density	60kg-130kg
Thickness	1mm-50mm
PVC Foam Style	Plain/Perforated/Grooved and Perforated/
Brand	Regal
Quality	High Strength
Price	Competitive
Shipping	Fast Shipping
Use	Yacht Building
Usage	Boat Building
Materials	PVC Foam
Size	2100X1020mm
Name	PVC Panel
Other Name	Foam Board
Transport Package	Carton or Wood
Specification	2100X1120mm
Trademark	regal
Origin	China
HS Code	3921129000
Production Capacity	5000000sqm

Product Description

High Strength 60/80/100/130/200kg/M3 PVC Core Foam yacht Construction boat pvc foam

Structural PVC Foam China Professional Environmental PVC Foam for Sandwich Panel

PVC foam, with unique closed cell and cross linked structure, has good properties of high stiffness, strength to weight ratio, superior toughness, low water absorption and excellent resistance to chemicals. the fine cell structure gives a good bonding surface. It is compatible with unsaturated polyester resin, epoxy resin, vinyl ester resin etc, and widely used in the applications of wind energy, aerospace, marine, automobile, train, sports goods and so on.

We will suggest different types according to your application.

Strucell P passed GL certification,ABS certification,DNV certification,DIN551,NFF16-101,ROHS,SGS.
Feature:
density:60 - 200 kg/m3
good performance in hardness
Excellent anti-fatigue resistance, good impact resistance, low suction rate, thermal insulation
Good flame retardant performance
It is not easy to be damp and mildew
Good dimensional stability and processability, suitable for the manufacturing process of various sandwich structures, and compatible with a variety of resin systems, is the ideal core of the lightweight composite sandwich structure
processing temperature-240ºC~+100ºC,Use temperature-240ºC~+80ºC

Item	Unit	P48	P60	P80	P100	P130	P200	P250
Density	Kg/m3	48	60	80	100	130	200	250
Density(Nominal)	Kg/m3	/	54	72	/	/	/	/
Tensile strength	Mpa	1.4	1.8	2.5	3.5	4.5	7.1	9.2
Tensile strength	Mpa	1.1	1.5	2.2	2.5	3.5	6.3	8
Tensile modulus	Mpa	55	75	95	130	175	250	360
Tensile modulus	Mpa	45	57	85	105	135	210	320
Compressive strength	Mpa	0.6	0.93	1.4	2	3	4.8	6.2
Compressive strength	Mpa	0.5	0.7	1.15	1.65	2.4	4.2	5.4
Compressive modulus	Mpa	50	70	90	135	170	240	300
Compressive modulus	Mpa	45	60	80	115	145	200	240
Shear strength	Mpa	0.5	0.76	1.15	1.44	2.1	3.5	4
Shear strength	Mpa	0.46	0.63	0.95	1.4	1.9	3.2	3.9
Shear modulus	Mpa	15	20	27	35	50	85	104
Shear modulus	Mpa	12	16	23	28	40	75	88
Shear elongation,at break	%	8	10	15	15	20	20	20
Shear elongation,at break	%	/	20	30	/	/	/	/